INTRODUCTION
PIB COMPOUND PT-60, PT-66 & PT-70 is a concentrate of very high molecular weight Polyisobutylene tackifier and Linear Low Density Polyethylene. The composition is used as a cling agent to produce stretchwrap films from LLDPE or LDPE. It is dry free flowing pellets. The high PIB content in the polymer matrix achieves the excellent cling property.
SPECIFICATIONS
Appearance : Lightly Powdered Translucent Dry Pellets
% PIB (active ingredient) : 58 ~ 72%
Loose Bulk Density : 0.45 ~ 0.50 gms/cm³
Specific Gravity : 0.910 ~ 0.920 gms/cm³
Moisture (at works) : < 0.5%
USAGE
PIB COMPOUND is designed to produce stretchwrap films from LLDPE, LDPE or any other Nonslip Polyolefins for the applications of Palletwrap and Silagewrap. It can be used on either blown film line or cast film process. PIB COMPOUND is mainly designed for the use where PIB is loaded separately through auto suction feeding. Polymers used with PIB COMPOUND must not contain any Anti blocking additive or slip agent as this will prevent the migration of cling additive on the films. Migration time for the good cling properties is usually 24 to 72 hours.
RECOMMENDED ADDITION
On monolayer blown film lines, 6% to 8% PT-60 by weight should be added to resin mix.
On monolayer Cast lines, 2% to 4% PIB COMPOUND by weight should be added.
On multilayer film lines, PIB COMPOUND is usually added to the skin layers only.
Addition level of PIB COMPOUND depends on which layer is used and the thickness of layer.
PACKING & STORAGE :
PIB COMPOUND is available in the packing of 25 kgs. laminated moisture proof woven sack bag.
Keep the product in cool & dry place with good ventilation. Away from the direct sunlight, high temperature, rain pour and not under heavy loads. Shelf life of PIB COMPOUND is about 12 months. Thereafter still it can be used, but with little higher dosage %ge than usual.
PIB COMPOUND PT-60, PT-66 & PT-70 is a concentrate of very high molecular weight Polyisobutylene tackifier and Linear Low Density Polyethylene. The composition is used as a cling agent to produce stretchwrap films from LLDPE or LDPE. It is dry free flowing pellets. The high PIB content in the polymer matrix achieves the excellent cling property.
SPECIFICATIONS
Appearance : Lightly Powdered Translucent Dry Pellets
% PIB (active ingredient) : 58 ~ 72%
Loose Bulk Density : 0.45 ~ 0.50 gms/cm³
Specific Gravity : 0.910 ~ 0.920 gms/cm³
Moisture (at works) : < 0.5%
USAGE
PIB COMPOUND is designed to produce stretchwrap films from LLDPE, LDPE or any other Nonslip Polyolefins for the applications of Palletwrap and Silagewrap. It can be used on either blown film line or cast film process. PIB COMPOUND is mainly designed for the use where PIB is loaded separately through auto suction feeding. Polymers used with PIB COMPOUND must not contain any Anti blocking additive or slip agent as this will prevent the migration of cling additive on the films. Migration time for the good cling properties is usually 24 to 72 hours.
RECOMMENDED ADDITION
On monolayer blown film lines, 6% to 8% PT-60 by weight should be added to resin mix.
On monolayer Cast lines, 2% to 4% PIB COMPOUND by weight should be added.
On multilayer film lines, PIB COMPOUND is usually added to the skin layers only.
Addition level of PIB COMPOUND depends on which layer is used and the thickness of layer.
PACKING & STORAGE :
PIB COMPOUND is available in the packing of 25 kgs. laminated moisture proof woven sack bag.
Keep the product in cool & dry place with good ventilation. Away from the direct sunlight, high temperature, rain pour and not under heavy loads. Shelf life of PIB COMPOUND is about 12 months. Thereafter still it can be used, but with little higher dosage %ge than usual.
Related Products
PPA MASTERBATCH (POLYMER PROCESSING AID)
UV MASTERBATCH (ULTRAVIOLET MASTERBATCH)
ANTIFOG MASTERBATCH
ANTISTATIC MASTERBATCH
SLIP MASTERBATCH
WHITE MASTERBATCH (TiO2 WHITE MASTERBATCH)
You may also like
Highest Rated Products
Back
Product Inquiry