低烟无卤电缆料相容剂

TRD-200GL Series Products
Product Introduction
The TRD-200GL series products are specially formulated polyolefin resin composites with functional resin substrates, produced through melt extrusion grafting of maleic anhydride monomers. These materials exhibit excellent polarity and reactivity, making them particularly suitable for low-smoke zero-halogen (LSZH) flame-retardant cable compounds.
Product Appearance
Milky white or light yellow particles ( Note: Under specific process conditions or during the run-in period after replacing screw elements and barrels in the equipment, intensified yellowing may occur, resulting in a more pronounced light yellow appearance.)
Product Specifications
Item Compatibilizer Performance Testing Cable Material Performance Testing
Model Density
（g/cm³） Melt Flow Rate （g/10min，190℃，2.16kg） Functional Group Content
(wt％) Tensile Strength (MPa) Elongation at Break（%） Tensile Strength (MPa) Elongation at Break （%） Recommended Addition Ratio（%）
TRD-200GL 0.931 0.5-1.0 0.8-1.2 21.0-23.0 780-820 12.5-14.0 180-220 6-8
TRD-201GL 0.930 0.3-0.8 0.6-1.0 22.0-26.0 720-780 11.5-12.5 180-220 6-8
TRD-202GL 0.932 0.3-1.0 0.8-1.2 24.0-27.0 730-780 11.0-12.5 180-220 6-8
Notes: The parameters listed are typical laboratory values. Actual performance may vary slightly depending on processing conditions, formulation systems and other factors.

Typical Applications
☆Used for calcium carbonate blended with inorganic materials such as aluminum hydroxide and magnesium hydroxide to fill polyolefin halogen-free cable materials;
☆Widely used in optical cable sheathing materials;
☆Compatibilizers for some low-smoke halogen-free cable insulating/sheathing materials;
☆Compatibilizers for some low-smoke halogen-free force cable materials;
☆Compatibilizers for some special low-smoke halogen-free cable materials.

---